BETOCHEM Filler (50-50)
| Description |
|---|
BETOCHEM Plamuur (Filler) is a non shrinking two-component filler based on solvent free epoxy, which is resistant to various chemicals and repaintable with different kinds of paint. BETOCHEM Plamuur (Filler) can be applied for horizontal and vertical repairs and is waterproof. Layers of 3mm BETOCHEM Plamuur(Filler)do have the same effect as 50 mm layer of concreteprotection |
| Quality control |
|---|
During manufacturing only raw materials of high quality are used which amply meet the strictest requirements. During the production process as well as during the final stages these materials are extensively tested for quality in our own laboratory. |
| Packaging and storage |
|---|
| 5, 7,5 en 15 kg and for plamuur 50/50 package 10 or 40 kg. In the original properly closed packaging in a cool dry place, frost free minimum storage life 6 months. |
| Precautions |
|---|
| Refer to the information on the packaging of the product, safety sheets and processing advice C. |
| Application |
|---|
| By means of a filling knife, trowel, float and brick jointer. |
| Resistance to chemicals |
|---|
| Refer to list of resistance to chemicals. |
| Articlecode | Plamuur-Filler |
|---|---|
| Colour | Concrete grey |
| Density [kg/dm³](20°C) | 1.7 |
| Amount to be used (kg/m²)(at 1 cm thickness of layer) | 17.0 |
| Thickness of layer | 3-40 |
| Solid content (percentage by volume) | 100 |
| Mixing ratio (by part of weight) | |
| • Component A | 79 |
| • Component B | 21 or |
| • Component A | 50 |
| • Component B | 50 |
| Flash point [°C](DIN 53213) | |
| Component A | > 100 |
| Component B | > 100 |
| Potlife [min] (20°C) | approx. 120 |
| Processing temperature [°C] | 10-35 |
| Processing temperature winter[°C] | 0-35 |
| Drying/full-hardening (20°C)/65% RH/7 mm thickness of layer) | |
| • dust dry | after approx. 8 |
| • repaintable | after approx. 24 |
| • ready tob e walked on | after approx. 24 |
| (in system building or with several layers, a maximum drying time of 24 hours between layers applies, unless a pre-treatment of the surface has occured) | |
| Compressive strength [N/mm²] | 63 |
| • after 24 hours at 5°C | 16 |
| • after 24 hours at 10°C | 27 |
| • after 24 hours at 20°C | 49 |
| Flexural-tensile strength [N/mm²] | 21 |
| E-module [N/mm²] | approx. 2873 |
| Shear strength [N/mm²] | 29,3 |
| Tensile strength [N/mm²] | 12 |
| Linear expansion coefficient [-5 K-1] | approx. 4.8 x 10 (-5) x K (-1) |
| Please contact us, we will send you the information. |
Liability
The technical instructions and recommendations we provide on the basis of our experience and to the best of our knowledge, are entirely without obligation and merely provide an indication. Not all facts, problems and queries that occur during practical application can be included in a general documentation sheet. Our recommendations and instructions do not commit us to any legal obligations as a result of the purchase and application of our products. Any deviating agreements made by our employees that are not included in our datasheets will only be lawful providing they have been confirmed in writing by the management. Our raw materials, semi-finished products and products comply with the most stringent quality standards. This does not relieve the user of their responsibility to test our products prior to their application. Our general trading and delivery conditions, which we are happy to forward to you on demand, are and remain applicable at all times.
This specification sheet supersedes any previous versions.